Grade：SP-22
1、Applications
a、Modifier for general purpose LLDPE：Garbage bags which generate less heat, flat yarn, inner film for laminated paper bags, shopping bags, adhesive tape etc..
b、PE industrial films, packing materials & containers etc.
2、Features
a、SP-22 is a LLDPE-based masterbatch containing 80% nano-precipitated calcium carbonate. It is grayish white with excellent dispersibility.
b、It can be mixed with PE resin for film blowing, casting, extrusion etc. and is easy to disperse with good compatibility. It functions as a modifier to improve the heat resistance, slip resistance, size stability, printability and texture. It also reduces heat release from burning, thus prevents secondary environmental pollution.
c、The printing, whitewash good; white opaque can reduce the amount of white pigment
3、Processing suggestions
a、General dosage recommended at 5~50 PHR with variation according to the products.
b、The processing temperature is set according to resin’s processing temperature and it applies well among 220±40℃.
4、Specifications：
|
Item |
Test method |
Unit |
Typical value |
|
Base |
----- |
----- |
LLDPE |
|
CaCO3 content |
----- |
% |
80 |
|
Specific gravity 23℃ |
GB1033-70 |
g/cm3 |
1.89 |
|
MI 2.16kg/190℃ |
GB3682-83 |
g/10mins |
7-8
..0 |
|
Moisture |
IR |
% |
< 0.2 |
|
Shape |
----- |
granule |
Ø2~3mm |
5、Applications
|
|
Sampling direction |
Thickness
(mm) |
Tensile strength (MPa) |
Yield strength (MPa) |
Elongation
％ |
|
Comparison samples |
Vertical |
0.025 |
42.5 |
22.1 |
460 |
|
Add SP-22，30Share |
Vertical |
0.025 |
45.6 |
24.8 |
481 |
6、Packing : 25kg/bag
Note：Use immediately once open to atmosphere. Keep away from moisture
|